%0 Journal Article
%T Microporosity Development of Herringbone Carbon Nanofibers by RbOH Chemical Activation
%A Vicente Jim¨¦nez
%A Paula S¨˘nchez
%A Fernando Dorado
%A Jos¨¦ Lu¨Şs Valverde
%A Amaya Romero
%J Journal of Nanotechnology
%D 2009
%I Hindawi Publishing Corporation
%R 10.1155/2009/373986
%X The influence of different activation conditions, including activating agent/CNFs ratio, activation temperature, and He flow rate, on the pore structure development of herringbone carbon nanofibers (CNFs) was studied. The best results of activated CNFs with larger specific surface area can be achieved using the following optimized factors: RbOH/CNFs ratio = 4/1, activation temperature = 900ˇăC ,and a He flow rate = 850 ml/min. The optimization of these three factors leads to high CNFs micropore volume, being the surface area increased by a factor of 3 compared to the raw CNFs. It is important to note that only the creation of micropores (ultramicropores principally) took place, and mesopores were not generated if compared with raw CNFs.
%U http://www.hindawi.com/journals/jnt/2009/373986/