%T Obtenci¨®n de microesferas biodegradables de ¨¢cido poli L-l¨¢ctico cargadas con doxorubicina Obtention of biodegradable microspheres of poly l-lactic acid loaded with doxorubicin
%A Dianelis Fern¨¢ndez Mena
%A Martha G¨®mez Carril
%A Diana Ramos Picos
%A Nict¨¦ Gonz¨¢lez Alfonso
%J Revista Cubana de Farmacia
%D 2005
%I ECIMED
%X Se ha demostrado que las microesferas biodegradables de ¨¢cido poli L-l¨¢ctico como portadores de f¨¢rmacos proporcionan una liberaci¨®n controlada y mantenida del principio activo, disminuyendo los efectos colaterales que estos pueden provocar. Por este motivo, se propuso evaluar la influencia de par¨¢metros como el rendimiento, la eficiencia de encapsulaci¨®n y el di¨¢metro medio de las part¨ªculas, en el proceso de preparaci¨®n de microesferas cargadas con doxorubicina, por el m¨¦todo de emulsi¨®n m¨²ltiple y evaporaci¨®n del solvente. Se comprob¨® que la concentraci¨®n de alcohol polivin¨ªlico y cloruro de sodio, as¨ª como la baja temperatura en la fase acuosa externa contribuyen a lograr mejores resultados en las caracter¨ªsticas f¨ªsico-qu¨ªmicas de las microesferas obtenidas. It has been proved that the biodegradable microspheres of poly l-lactic acid as drug carriers provide a controlled and maintained release of the active principle, reducing the side effects they may cause. For this reason, it was proposed to evaluate the influence of parameters such as performance, encapsulation efficiency and mean diameter of the particles, in the process of preparation of microspheres loaded with doxorubicin by the method of multiple emulsion and evaporation of the solvent. It was proved that the concentration of polyvinyl alcohol and sodium chloride, as well as the low temperature in the external aqueous phase, contribute to attain better results in the physical and chemical characteristics of the obtained microspheres
%K Microesferas
%K pol¨ªmeros
%K emulsi¨®n m¨²ltiple
%K evaporaci¨®n
%K Microspheres
%K polymers
%K multiple emulsion
%K evaporation