%0 Journal Article
%T Chemical solution-derived SrMg2(PO4)2:Eu2+ blue phosphor for ultraviolet emitting diodes
%A Kyu-Seog Hwang
%A Seung Hwangbo
%A Jin-Tae Kim
%J Optica Applicata
%D 2010
%I 
%X Eu2+-doped SrMg2(PO4)2 phosphor with blue emission was prepared by the low temperature chemical solution process using inorganic salts as a starting material. Transparent sol was preheated at 300 ˇăC for 120 min and then precursor was finally annealed at 900 ˇăC for 240 min in a reducing CO atmosphere. Crystallinity, surface morphology and luminescent properties have been investigated. The phosphor emits bright blue luminescence with a peak wavelength at 423 nm under near-ultraviolet excitation at 363 nm.
%K SrMg2(PO4)2
%K phosphor
%K blue
%K sol&ndash
%K gel