%T Experimental Study on Friction Characteristics of a Fibre Reinforced Composite Brake Pad<br>纤维增强合成闸片摩擦磨损特性的试验研究
%A LIANG Shuang
%A CHEN Guang-xiong
%A DAI Huan-yun
%A ZENG Jing
%A <br>梁爽
%A 陈光雄
%A 戴焕云
%A 曾京
%J 摩擦学学报
%D 2006
%I 
%X A series of brake friction tests on a fibre reinforced composite brake pad and a HZ408 brake pad materials rubbing against a brake disc material were carried out on a friction and wear tester of MM-1000 type.During the test,the coefficient of friction,temperature increment and wear mass loss of both materials were measured.The worn surface morphologies were observed using a Confocal Laser Scanning Microscope(CLSM).The initial brake speed had a smaller influence on the friction coefficient of the fibre reinforced composite than it exerted the influence on that of the HZ408 brake pad.The fibre reinforced composite exhibited a larger averaged friction coefficient than the HZ408 brake pad did at a high speed.The wear mass loss of the fibre reinforced composite was found to be slightly larger than that of the HZ408 brake pad.At a low speed,the temperature increments of both pad materials were close to each other.At a high speed,the temperature increment of the fibre reinforced composite was found to be slightly larger than that of the HZ408 brake pad.
%K disc brake
%K friction coefficient
%K wear
%K composite pad<br>盘形制动
%K 摩擦系数
%K 磨损
%K 合成闸片
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=6E709DC38FA1D09A4B578DD0906875B5B44D4D294832BB8E&cid=5D344E2AD54D14F8&jid=2F467A5C6371C830162AAA01D7DAD07A&aid=888871C1F6A075B1&yid=37904DC365DD7266&vid=96C778EE049EE47D&iid=B31275AF3241DB2D&sid=C7461453A367FC85&eid=65FC738C50B41E43&journal_id=1004-0595&journal_name=摩擦学学报&referenced_num=1&reference_num=10