%X A phenomenon is present in the industrial applications that the surface with lowerhardness shows a better wear-resistance than the surface with higher hardness. In order to clarify itsmechanism,the surface strengthening effect of a substrate with lower hardness in wear process wasinvestigated by using the fixed and free abrasives separately. Under the given test condition,boththe fixed and free abrasives can form an abrasive/iron composite mate rial layer on the surface ofspecimens,in consequence,their hardness and wear-resistance can be increased and their servicelife can be lengthened. The bigger the fixed a brasives,the casier the formation of this compositematerial layer. The effect of in creasing weight is m ore obvious for the free abrasives,and thethickness of the composite lay er is al so larger.The formation mechanism of composite layer ismainly due to the embedmen t and crack of abrasives and mixing with the iron substrate in thedeformation process induced by other big a brasives.The analvsis by EDX found that the ratios ofabrasives to iron in the composite layers are 2:1 regardless the abrasives are fixed or free,becausethe composite layer will peel off due to the damage of continuity of iron substrate when this ratiowas surpassed.Therefore,this surface strengthening measure by forming a composite material layercan be employed in practice very e conomically for lengthening the service life of machinecomponents in the condition of not too severe abrasive wear.
%K abrasive wear
%K composite materials
%K strengthening effet
%K wear-resistance<br>磨粒磨损
%K 复合材料
%K 耐磨性
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=6E709DC38FA1D09A4B578DD0906875B5B44D4D294832BB8E&cid=5D344E2AD54D14F8&jid=2F467A5C6371C830162AAA01D7DAD07A&aid=C18DDAA7F43096806781031E99216FD5&yid=BBCD5003575B2B5F&vid=23CCDDCD68FFCC2F&iid=38B194292C032A66&sid=AD16A18DBD734D13&eid=E089FDF3CDAE8561&journal_id=1004-0595&journal_name=摩擦学学报&referenced_num=1&reference_num=4