%0 Journal Article
%T Texture and magnetostriction in rolled Fe-Ga based alloy<br>
%A Gao Xue-xu
%A <br>
%J 金属学报
%D 2008
%I 
%X The addition of Nb was used to improve ductility during rolling process. The (Fe81Ga19)+1at.%Nb sheet with thickness of 0.6 mm was prepared by conventional rolling, including hot rolling and cold rolling. Results that demonstrate the rolled texture, recrystallization texture and magnetostriction of (Fe81Ga19)+1at.%Nb sheets are presented in this work. The as-rolled sheet had {111} and near {001}<110> rolling-texture grains, and had magnetostriction only as 26×10-6. A near {011}<100> texture and a {001}<100> texture were formed in recrystallized sheets which were water quenched after two hours annealed at 1250 °C and1300 °C, and their magnetostriction (3/2) s were 106×10-6and136×10-6 respectively.
%K Fe-Ga alloy
%K rolling
%K texture
%K magnetostriction<br>
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=AB188D3B70B071C57EB64E395D864ECE&jid=B061E1135F1CBDEE96CD96C109FEAD65&aid=429D012C74CF68EC211350BD84A1EED2&yid=67289AFF6305E306&vid=1AE5323881A5ECDC&iid=9CF7A0430CBB2DFD&sid=D7513DBF373F2B6C&eid=78996380F3108204&journal_id=0412-1961&journal_name=金属学报&referenced_num=0&reference_num=0