%0 Journal Article
%T Effect of tin content on microstructures and mechanical properties of Ti(C,N)/NiCr cermets<br>TiN含量对Ti(C,N)/NiCr金属陶瓷微观结构和力学性能的影响
%A WANG Quanzhao
%A LIU Yue
%A GUAN Dehui
%A YU Baohai
%A CHEN Zhiliang
%A BI Jing
%A <br>王全兆
%A 刘 越
%A 关德慧
%A 于宝海
%A 陈志亮
%A 毕 敬
%J 金属学报
%D 2005
%I 
%X Ti(C,N)/NiCr cermets were vacuum sintered by powder metallurgy technology. The effects of TiN additions on microstructures and mechanical properties of Ti(C, N)/NiCr cermets were investigated. Results revealed that the hard phase particles were refined and the morphology of the particles changed from a circular to a polygonal shape by the additions of TiN because of the formation of Ti(C,N) solid solution; With increasing TiN additions, the bonding strength increased to the maximum values at 4%TiN content during low sintering temperature and at 6%TiN content during high sintering temperature, respectively, and then decreased. Hardness changed little when TiN addition was less than 10%, but decreased dramatically when TiN addition exceeded 10%. Fracture photograph showed that trans-granular fracture was the main failure mode because of the good interface bonding strength between binding phase and ceramic hard phase.
%K Ti(C
%K N)/NiCr
%K cermet
%K microstructure
%K mechanical property<br>Ti（C
%K N）／NiCr
%K 金属陶瓷
%K 微观结构
%K 力学性能
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=AB188D3B70B071C57EB64E395D864ECE&jid=B061E1135F1CBDEE96CD96C109FEAD65&aid=6FE65E7C25111ABE&yid=2DD7160C83D0ACED&vid=2001E0D53B7B80EC&iid=708DD6B15D2464E8&sid=F88EF6DD822B0FF5&eid=6BF76AE9E086F688&journal_id=0412-1961&journal_name=金属学报&referenced_num=6&reference_num=15