%T EFFECT OF HYDRIDE AND HYDROGEN-INDUCED MARTENSITE ON FRACTURE TOUGHNESS OF TiNi ALLOY<br>Effect of Hydride and Hydrogen—Induced Martensite on Fracture Toughness of TiNi Alloy
%A HE Jianying
%A GAO Kewei
%A QIAO Lijie
%A CHU Wuyang
%A <br>何健英
%A 高克玮
%A 乔利杰
%A 褚武扬
%J 金属学报
%D 2004
%I 
%X The hydride formed in hydrogen charging TiNi shape memory alloy could decrease evidently fracture toughness K IC of the TiNi alloy and the relative loss of K IC is as high as 96%. The relative loss of K IC induced by the hydrogen induced martensite, however, is only about 1.8%, and does not change evidently with hydrogen concentration. Therefore, the decrease in fracture toughness of hydrogenated specimen is almost completely attributed to hydride. The relative loss of induced by hydrides, increases with increasing hydride content. Microcracks could be generated along the hydrides during charging at i>15 mA/cm2 and do not cause farther the decrease in K IC .
%K TiNi
%K hydrogen
%K hydride
%K hydrogen-induced martensite
%K fracture toughness<br>TiNi
%K 氢
%K 氢化物
%K 氢致马氏体
%K 断裂韧性
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=AB188D3B70B071C57EB64E395D864ECE&jid=B061E1135F1CBDEE96CD96C109FEAD65&aid=8884A89DF4DAEB25&yid=D0E58B75BFD8E51C&vid=1371F55DA51B6E64&iid=38B194292C032A66&sid=6490F0E20C4B41AD&eid=AF507FDD66D991DA&journal_id=0412-1961&journal_name=金属学报&referenced_num=0&reference_num=14