%0 Journal Article
%T POLYIONIC COMPLEXES DERIVED FROM POLYVINYL ALCOHOL IV. MECHANICAL BEHAVIOR AND PERMEABILITY OF POLYIONIC COMPLEXES MEMBRANES PREPARED FROM PVA AND ETHYLENE-VINYL ALCOHOL COPOLYMER<br>聚乙烯醇衍生的聚离子复合物的研究——Ⅳ.聚离子复合物膜的力学行为及透过性能
%A WANG Lin
%A DING Hong
%A LI Fu-mian
%A <br>王林
%A 丁虹
%A 李福绵
%J 高分子学报
%D 1993
%I 
%X The mechanical behavior of polyionic complex (PIC)membranes derived from polyvinyl alcohol(PVA) or ethylene-vinyl alcohol copolymer (EVA) have been investigated. The presence of ethylene block segment in the backbone of polyions can endow PIC membranes with more toughness. Increasing the degree of substitution of the polyions, the formed PIC becomes harder and more brittle. Under the environment of relative humidity (R. H. ) of 40%, the tensile strength, relative elongation and modulus of PICs are at about 300kg/cm2,10% and 8×103kg/cm2,respectively,whereas inthe environment of 90% R.H.M these of PICs derived from EVA are at about 90 kg/cm2,150% and 13kg/cm2,respectively,better than that of PVA derived polyionic membrane and ordinary PIC such as Ioplex 101. The permeabil-ity of PIC membranes derived from EVA have also been studied.
%K 聚乙烯醇
%K 共聚
%K EVA
%K 聚离子复合物
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=6E709DC38FA1D09A4B578DD0906875B5B44D4D294832BB8E&cid=6579068328FE643F&jid=15971983683C7643EE80F1CE621DEB60&aid=64948160A9F2DFDAA1AAA5A75231CE27&yid=D418FDC97F7C2EBA&iid=B31275AF3241DB2D&sid=04CF423CEE45E258&eid=A8E9231F98774741&journal_id=1000-3304&journal_name=高分子学报&referenced_num=2&reference_num=2