%T PLASMA POLYMERIZATION OF METHANE AND POLYMER STRUCTURE<br>甲烷的等离子体聚合及聚合物结构的研究
%A LU Li-zhen
%A CHEN Jie
%A ZHANG Yong-he
%A LIU Xue-shu
%A <br>卢丽珍
%A 陈捷
%A 张永和
%A 刘学恕
%J 高分子学报
%D 1986
%I 
%X In a capacitively coupled discharge with external electrodes, plasma polymerization of methane was studied. It was found that polymer deposition rate was accelerated when haloids were added in plasma, and effect of polymerization condition on the polymer deposition rate was confirmed at the same time. Results from IR, X-ray diffraction and elementary analysis show that plasma polymerized methane (PPM) has a cross-linked structure. PPM films have good thermostability. Refractive index and density of PPM films were determined byestablish-ed ellipitical polarization are 1.55 and 1.11 g/cm3respectively.
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=6E709DC38FA1D09A4B578DD0906875B5B44D4D294832BB8E&cid=6579068328FE643F&jid=15971983683C7643EE80F1CE621DEB60&aid=5A3446FD91B99212&yid=4E65715CCF57055A&iid=94C357A881DFC066&sid=23410D0BDB501DF5&eid=5F8BAECF36EB55E2&journal_id=1000-3304&journal_name=高分子学报&referenced_num=0&reference_num=0