%T FAILURE ANALYSIS FOR CORROSION CRACKING OF A HEAT- EXCHANGER OF STAINLESS STEEL<br>波纹不锈钢换热板腐蚀开裂失效分析
%A XIONG Jin-ping
%A ZUO Yu
%A HU Ding-zhu
%A <br>熊金平
%A 左禹
%A 胡定铸
%J 腐蚀科学与防护技术
%D 2005
%I 
%X The appearance of the failed heat - exchanger of stainless steel was examined by naked eye, the morphology and feature of the fracture of the failed heat - exchanger of stainless steel were obtained by SEM, the element content of the corrosion product on the fracture and the scales on the stainless steel were also analyzed. The IR result indicted that the rubber seal gasket was made of polychloroprene, which can be decomposed to produce Cl^- at high temperature. The overall analysis result showed that stress corrosion cracking was induced by Cl^-, the cracks were trans - granular mainly but there were also inter- granular cracks.
%K stalnless steel
%K heat - exchanger
%K stress corrosion crack
%K failure analysis<br>不锈钢
%K 换热器
%K 应力腐蚀开裂
%K 失效分析
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=AB188D3B70B071C57EB64E395D864ECE&jid=9F6E6EC8BA5BB62698F6640073DDD6E1&aid=A157483733C26978&yid=2DD7160C83D0ACED&vid=BCA2697F357F2001&iid=B31275AF3241DB2D&sid=8D75AD3BD0D1BCC5&eid=B40AD8FE6FA88DE9&journal_id=1002-6495&journal_name=腐蚀科学与防护技术&referenced_num=1&reference_num=5