%T FAILURE ANALYSIS OF TURBINE BLADES FOR A HEAT-POWER PLANT<br>热电厂汽轮机叶片断裂原因分析
%A 张亚明
%A 夏邦杰
%A 董爱华
%A 徐一宁
%J 腐蚀科学与防护技术
%D 2009
%I 
%X Failure analysis of turbine blades for a heat-power plant of a petrochemical company was conducted by macroscopic and metallographic observations,chemical composition analysis,as well as SEM examination with EDAX analysis. The results showed that the fracture of turbine blades is caused by corrosion fatigue. The pits on the blade induced the initiation of cracks and then facilitate crack propagation at these sites. However the pitting corrosion of the blades was caused by the chloride and sulfur existed in the steam.
%K turbine blade
%K 2Cr13 stainless steel
%K pitting
%K corrosion fatigue
%K fracture<br>汽轮机叶片
%K 2Cr13不锈钢
%K 点蚀
%K 腐蚀疲劳
%K 断裂
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=AB188D3B70B071C57EB64E395D864ECE&jid=9F6E6EC8BA5BB62698F6640073DDD6E1&aid=00B3BEC1FBB49DAF677FE850B6B816C6&yid=DE12191FBD62783C&vid=659D3B06EBF534A7&iid=B31275AF3241DB2D&sid=4081E94A71AB3C30&eid=106103EB0EA31435&journal_id=1002-6495&journal_name=腐蚀科学与防护技术&referenced_num=1&reference_num=0