%0 Journal Article
%T Microstructures and Mechanical Properties of Si-Al-Mn TRIP Steel with Niobium<br>Microstructures and Mechanical Properties of Si-AI-Mn TRIP Steel with Niobium
%A Zhengyou TANG
%A Hua DING
%A Linxiu DU
%A Long LI
%A <br>Zhengyou
%A TANG
%A Hua
%A DING
%A Linxiu
%A DU
%A Long
%A LI
%J 材料科学技术学报
%D 2007
%I 
%X Microstructure consisting of ferrite, bainite and retained austenite can be obtained through intercritical annealing and isothermal treatment in bainite transformation region for low silicon TRIP (transformation induced plasticity) steel containing niobium. Effects of strain rate, Nb content and soaking temperature in bainite region on microstructure and mechanical properties of test steels were investigated. It is shown that as strain rate ranges from 10-2 to 10-4 s-1, the volume fraction of transformed martensite from retained austenite, as well as tensile strength, elongation rate and strength-ductility product, increases. When Nb is added, the volume fraction of retained austenite decreases, but tensile strength and yield strength increase. While Nb content reaches 0.014%, the steel exhibits high elongation and combination of strength and ductility. Higher retained austenite volume fraction and good mechanical properties are obtained in the test steels when the soaking temperature in bainite region is 400oC. The maximum values of tensile strength, total elongation rate and strength-ductility product can reach 739 MPa, 38% and 28082 MPa%, respectively.
%K TRIP
%K Strain rate
%K Niobium content
%K Retained austenite
%K Mechanical properties<br>显微结构
%K Si-AI-Mn合金
%K 机械力学
%K 铌元素
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=84529CA2B2E519AC&jid=324DC3CAB22330DB19158AE0A9B7BFA5&aid=F1839B40C8AE1F67A49EDA646B21C506&yid=A732AF04DDA03BB3&vid=EA389574707BDED3&iid=B31275AF3241DB2D&sid=C8C16F05E379B334&eid=89FA2FA9891FF61E&journal_id=1005-0302&journal_name=材料科学技术学报&referenced_num=0&reference_num=23