%0 Journal Article
%T Oxygen Behavior in Bulk Amorphous Zr-base Alloy<br>Oxygen Behavior in Bulk Amorphous Zr—base Alloy
%A Keqiang QIU
%A Qingsheng ZHANG
%A Aimin WANG
%A Haifeng ZHANG
%A Bingzhe DING
%A Zhuangqi HU
%A <br>Keqiang QIU
%A Qingsheng ZHANG
%A Aimin WANG
%A Haifeng ZHANG
%A Bingzhe DING and Zhuangqi HUState Key Laboratory of RSA
%A Institute of Metal Research
%A Chinese Academy of Sciences
%A Shenyang
%A ChinaLiaoning Institute of Technology
%A Jinzhou
%A China[
%J 材料科学技术学报
%D 2002
%I 
%X Bulk Zr55Al10Ni5Cu30 metallic glass plates with a dimension of 85 mm×35mm×4 mm and a complicated plate werefabricated by injecting casting method using spongy zirconium and industrial purity aluminum, nickel and copper asraw materials. It was shown that the holding time of liquid metals at elevated temperatures had a great influence onthe oxygen content of the plates due to the contamination resulting from the atmosphere. Increasing holding timeresulted in the increase of oxygen content in the injected alloy. The glass transition temperatures of the bulk metallicglass plates are higher than that reported in the literature and crystallization temperature is lower for the one withhigher oxygen content at the same heating rate. The extension of the undercooled liquid region △Tx reaching about87 K is 3 K higher than that previously reported and 26 K higher than that with oxygen content of 0.076 wt pct forthe one with oxygen content as high as 0.065 wt pct. Therefore the oxygen content of the alloy has a significantinfluence on the glass forming ability and thermal stability of bulk metal glass. It is suggested that direct correlationbetween high glass forming ability and large △Tx is only valid for a well-defined Iow oxygen concentration or has tobe reconsidered by incorporating oxygen as an additional alloying element.
%K Zr-base amorphous alloy
%K Oxygen
%K Undercooling<br>铝基合金
%K 氧化行为
%K 冷却
%K 合金元素
%K Zr55Al10Ni5Cu30
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=84529CA2B2E519AC&jid=324DC3CAB22330DB19158AE0A9B7BFA5&aid=34FEF98F5BF1CAB7EB9EEEB7D137DA77&yid=C3ACC247184A22C1&vid=13553B2D12F347E8&iid=CA4FD0336C81A37A&sid=08805F9252973BA4&eid=BB0EA31DB1B01173&journal_id=1005-0302&journal_name=材料科学技术学报&referenced_num=0&reference_num=0