%T Effects of Pressure on the Solidification Microstructure of Mg65Cu25Y10 Alloy<br>Effects of Pressure on the Solidification Microstructure of Mg_(65)Cu_(25)Y_(10) Alloy
%A Jia ZHANG
%A Keqiang QIU
%A Aimin WANG
%A Haifeng ZHANG
%A Mingxiu QUAN
%A Zhuangqi HU
%A <br>Jia ZHANG
%A Keqiang QIU
%A Aimin WANG
%A Haifeng ZHANG
%A Mingxiu QUAN and Zhuangqi HU Shenyang National Laboratory for Materials Science
%A Institute of Metal Research
%A Chinese Academy of Sciences
%A Shenyang
%A China
%J 材料科学技术学报
%D 2004
%I 
%X The Mg65Cu25Y10 melts were quenched at a temperature of 973 K under various pressures in the range of 2～5 GPa and ambient pressure. The microstructure of the solidified specimens has been investigated by X-ray diffraction,transmission electron microscope and electron probe microanalysis. Experimental results show that the pressure has a great influence on the solidification microstructure of the Mg65Cu25Y10. At ambient pressure, the solidification products are Mg2(Cu,Y) and a very small amount of Y2O3 inclusion. As the pressure is above 2 GPa, a new Cu2(Y,Mg) phase appears, while Y2O3 is not observed at the pressure of 3, 4 and 5 GPa. When the pressure increases from 2 GPa to 5 GPa, the grain sizes of Mg2(Cu,Y) and Cu2(Y,Mg) decrease from 125, 96 nm to 80,7 nm, respectively. The mechanisms for the effects of the pressure on the phase evolution and microstructure during solidification process of Mg65Cu25Y10 alloy have been discussed.
%K Mg65Cu25Y10 alloy
%K Solidification
%K Glass formation alility<br>
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=84529CA2B2E519AC&jid=324DC3CAB22330DB19158AE0A9B7BFA5&aid=18599AE56B1871A5&yid=D0E58B75BFD8E51C&vid=A04140E723CB732E&iid=CA4FD0336C81A37A&sid=F24949CFDB502409&eid=6270DC1B5693DDAF&journal_id=1005-0302&journal_name=材料科学技术学报&referenced_num=0&reference_num=18