%T Microstructure and Properties of(Ti,Al,Zr)N Multi-components Hard Reactive Films with N-gradient Distributions
(Ti,Al,Zr)N多元氮梯度硬质反应膜的组织结构和性能
%A L Huimin ZHANG Jun College of Mechanical Engineering
%A Shenyang University
%A Shenyan Key Laboratory of Materials Modification by Laser
%A Ion
%A Electron Beams Ministry of Education
%A Dalian University of Technology
%A Dalian
%A
吕会敏
%A 张钧
%J 材料研究学报
%D 2011
%I
%X (Ti, Al, Zr)N multi–component hard films with N–gradient distributions were prepared by multi arc ion plating (MAIP) technology using the combined pure Zr and Ti–Al alloy targets. The surface and cross–fracture morphology, the surface compositions and the phase structure of the as–deposited films were observed and measured. The effects of bias voltage on the film quality, phase structure, the micro–hardness, the adhesion between film and substrate and the thermal shock resistance were investigated. In comparison with TiN, (Ti, Al)N and (Ti, Zr)N films, the as–deposited (Ti,Al,Zr)N films from the combination of pure Zr and Ti–Al alloy targets exhibited higher micro–hardness values even up to HV6000. Each of the as–deposited films has very high adhesion strength, in terms of critical load, larger than 180 N. The good heat shock resistance was also reached for each of the as–deposited films.
%K surface and interface in the materials
%K
%K (Ti
%K Al
%K Zr)N films
%K multi&ndash
%K arc ion plating
%K micro&ndash
%K hardness
%K thermal shock
材料表面与界面
%K (Ti
%K Al
%K Zr)N膜
%K 多弧离子镀
%K 显微硬度
%K 热震
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=84529CA2B2E519AC&jid=C101C4C04993B4D94FCD8446E6CBEB3B&aid=3924FE186C90DEE42C66B682C382E8A1&yid=9377ED8094509821&vid=C5154311167311FE&iid=CA4FD0336C81A37A&sid=CFAC5CB624A41AFD&eid=BB0EA31DB1B01173&journal_id=1005-3093&journal_name=材料研究学报&referenced_num=0&reference_num=0