%T Degradation of alumina formed on Fe–15Cr–10Al alloy induced by chlorine and sulfur in atmospheres<br>气氛中硫和氯导致Fe-15Cr-10Al合金表面氧化铝膜退化
%A PAN Taijun
%A NIU Yan
%A <br>潘太军
%A 牛焱
%J 材料研究学报
%D 2008
%I 
%X The corrosion behavior of Fe–15Cr–10Al alloy was examined at 700 °C in the reducing H2--CO2  and H2--HCl--H2S--HClatmosphere. As a result, the minor addition of HCl and H2S to a H2--CO2 atmosphere induced the degradation of protective alumina and the growth of Fe, Cr and Al oxide mixtures on the surface of Fe–15Cr–10Al alloy, which was attributed to the formation of sulfides  and chlorides in the scales during corrosion procedure. The equilibrium partial pressures of  chlorine, oxygen and sulfur in the mixed gases were calculated to estimate the possible reactions  between the alloy components and the multi–reactants, and their corrosion mechanisms were  also interpreted.
%K materials failure and protection
%K Fe-Cr-Al alloy
%K chlorine
%K sulfur
%K degradation<br>材料失效与保护
%K Fe-Cr-Al合金
%K 氧化
%K 氯
%K 硫
%K 退化
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=84529CA2B2E519AC&jid=C101C4C04993B4D94FCD8446E6CBEB3B&aid=C12A2EFE62AF72B01688302E857D7930&yid=67289AFF6305E306&vid=BC12EA701C895178&iid=B31275AF3241DB2D&sid=6EEC242D0D8BE428&eid=44E78A5D1B37D836&journal_id=1005-3093&journal_name=材料研究学报&referenced_num=0&reference_num=13