%0 Journal Article %T A Study on the Cross-Polarization Kinetics of Polyethylene Crystals
聚乙烯结晶区的交叉极化动力学研究 %A LIU Zhi-jian %A SHU Jie %A ZHANG Li-li %A CHEN Qun %A
刘志建 %A 舒婕 %A 张莉莉 %A 陈群 %J 波谱学杂志 %D 2008 %I %X The kinetics of cross-polarization (CP) between 1H and 13C nuclei in the crystalline regions of elongated polyethylene fiber was studied. It was found that, with a moderate magic angle spinning (MAS) rate, the CP build-up curves of both orthorhombic and monoclinic crystals of PE can be described by I-I*-S- model. For the fiber sample aligning with the MAS axis in the rotor, the CP build-up curves of both orthorhombic and monoclinic crystals exhibit oscillation, while those of the disoriented samples exhibit monotonic increase. These results demonstrated that, to a certain extent, both orthorhombic and monocline crystals are oriented along the direction of elongation. The degree of orientation of the monoclinic crystal is higher than that of the orthorhombic crystal. Measurement of the kinetics of cross-polarization can be employed as a new technique to determine the degree of orientation of polymer chain. %K 固体NMR %K 交叉极化动力学 %K 聚乙烯 %K 取向 %U http://www.alljournals.cn/get_abstract_url.aspx?pcid=6E709DC38FA1D09A4B578DD0906875B5B44D4D294832BB8E&cid=47EA7CFDDEBB28E0&jid=1A3C8C6E452BD1AF5A6B6B99BA3989C9&aid=4E7328801FC3620DEDB961ADF1C6A252&yid=67289AFF6305E306&vid=C5154311167311FE&iid=0B39A22176CE99FB&sid=BA79719BCA7341D5&eid=F260CE035846B3B8&journal_id=1000-4556&journal_name=波谱学杂志&referenced_num=0&reference_num=23