%T Status on the Unidirectionally Solidified Eutectic Composite<br>定向凝固共晶多相复合陶瓷的研究现状
%A PAN Zhen-Su
%A ZHANG Hui-Feng
%A GUO Jing-Kun
%A <br>潘振甦
%A 张惠丰
%A 郭景坤
%J 无机材料学报
%D 1999
%I Science Press
%X This paper reviews the manufacturing method of the unidirectionally solidified eutectic composite. A unidirectionally solidified Al_2O_3/YAG eutectic composite has superior flexural strength, thermal stability and creep resistance at high-temperature up to 2073K. For example, the flexural strength is 350--400MPa indepedent of testing temperature from room temperature to 2073K (just below its melting point of 2100K). During tensile test above 1923K, the eutectic composite shows the evidence of plastic deformation occurring by dislocation motion, and a yield phenomenon similar to many metals observed. The microstructure of the composite is extremely stable after heat treatment at 1973K for 1000h in air atmosphere. It may be expected that it would be a new heat-resistant structural material in the twenty-one century.
%K unidirectional solidification
%K eutectic
%K alumina
%K garnet
%K composite<br>定向凝固
%K 共晶
%K 复合陶瓷
%K 多相复合
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=84529CA2B2E519AC&jid=ABC0063016AF57E1C73EF43C8D2212BD&aid=894D70E4A6F117E7B81EFDAC30DF5ABC&yid=B914830F5B1D1078&vid=F3583C8E78166B9E&iid=E158A972A605785F&sid=F9A6B6F259CE5121&eid=89389F643CA3F778&journal_id=1000-324X&journal_name=无机材料学报&referenced_num=4&reference_num=12