%0 Journal Article
%T Microstructure and Mechanical Properties of TiB2/FeMo Cermet<br>TiB2/FeMo陶瓷的显微结构与力学性能
%A MIAO Ming-Qing
%A FU Zheng-Yi
%A ZHANG Jin-Yong
%A GONG Lun-Jun
%A <br>苗明清
%A 傅正义
%A 张金咏
%A 龚伦军
%J 无机材料学报
%D 2005
%I Science Press
%X TiB2 cermet containing 7wt% Fe and 3wt% Mo was fabricated by hot pressing. The effects of sintering temperature, holding time on microstructure and mechanical properties were investigated, the densifacation process during sintering was analysed. The experimental results show that the bending strength and the Rockwell hardness reveal a peak value with the sintering temperature rising up; with holding time prolonged, the bending strength decreases slightly. The densification rate is the fastest in the rearrangement stage during liquid sintering.
%K cermet
%K densification
%K hot pressing
%K microstructure<br>金属陶瓷
%K 致密化
%K 热压烧结
%K 显微结构
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=84529CA2B2E519AC&jid=ABC0063016AF57E1C73EF43C8D2212BD&aid=8371E939BF739E1D&yid=2DD7160C83D0ACED&vid=A04140E723CB732E&iid=0B39A22176CE99FB&sid=A03A15CF5604A8B0&eid=51F9E747BA1ACB45&journal_id=1000-324X&journal_name=无机材料学报&referenced_num=3&reference_num=17