%T Influence of aggregation structure and traps on surface flashover of XLPE in vacuum<br>聚集态和陷阱对交联聚乙烯真空沿面闪络特性的影响
%A Li Sheng-Tao
%A Huang Qi-Feng
%A Sun Jian
%A Zhang Tuo
%A Li Jian-Ying
%A <br>李盛涛
%A 黄奇峰
%A 孙健
%A 张拓
%A 李建英
%J 物理学报
%D 2010
%I 
%X In the paper, the influence of aggregation structure and traps on both DC and impulse flashover voltage of semi-crystalline cross-linked polyethylene (XLPE) in vacuum are investigated. After heat t at 135 ℃ for 10min, the XLPE samples were quenched to -56 ℃ or -25 ℃, cooled normally, cooled at a rate of 1 ℃/min or 0.5 ℃/min to room temperature, respectively. The electrical properties, microstrueture and trap distribution of heat-treated samples were studied. Compared with untreated samples, it is found that the dc and impulse flashover voltages of heat treated samples are raised by 76% and 19%, respectively. It is proposed that the aggregation structure and trap level is changed by heat treatment, leading to the improvement of surface flashover properties in vacuum. It is suggested that the vacuum flashover characteristics can be improved by controlling the aggregation structure and trap levels of seml-crystalline polymers.
%K XLPE
%K surface flashover
%K aggregation structure
%K trap<br>交联聚乙烯，
%K 真空沿面闪络，
%K 聚集态，
%K 陷阱
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=6E709DC38FA1D09A4B578DD0906875B5B44D4D294832BB8E&cid=47EA7CFDDEBB28E0&jid=29DF2CB55EF687E7EFA80DFD4B978260&aid=F2EC8651E69950F40661686F0B53B74E&yid=140ECF96957D60B2&vid=6AC2A205FBB0EF23&iid=CA4FD0336C81A37A&sid=B941678158018439&eid=9BA67A0B76A3DBA8&journal_id=1000-3290&journal_name=物理学报&referenced_num=0&reference_num=0