%T Improving poor fill factors for solar cells via light-induced plating
光诱导镀改善太阳电池填充因子的研究
%A Xing Zhao
%A Jia Rui
%A Ding Wuchang
%A Meng Yanlong
%A Jin Zhi
%A Liu Xinyu
%A
邢钊
%A 贾锐
%A 丁武昌
%A 孟彦龙
%A 金智
%A 刘新宇
%J 半导体学报
%D 2012
%I
%X Silicon solar cells are prepared following the conventional fabrication processes, except for the metallization firing process. The cells are divided into two groups with higher and lower fill factors, respectively. After light-induced plating (LIP), the fill factors of the solar cells in both groups with different initial values reach the same level. Scanning electron microscope (SEM) images are taken under the bulk silver electrodes, which prove that the improvement for cells with a poor factor after LIP should benefit from sufficient exploitation of the high density silver crystals formed during the firing process. Moreover, the application of LIP to cells with poor electrode contact performance, such as nanowire cells and radial junction solar cells, is proposed.
%K solar cells
%K light-induced plating
%K fill factor
%K silver crystal
硅太阳能电池
%K 填充因子
%K 扫描电子显微镜
%K 电镀
%K 光致
%K 烧制过程
%K LIP
%K 银电极
%U http://www.alljournals.cn/get_abstract_url.aspx?pcid=5B3AB970F71A803DEACDC0559115BFCF0A068CD97DD29835&cid=1319827C0C74AAE8D654BEA21B7F54D3&jid=025C8057C4D37C4BA0041DC7DE7C758F&aid=86F358091BA7D2A93425EECB1C2F1265&yid=99E9153A83D4CB11&vid=27746BCEEE58E9DC&iid=9CF7A0430CBB2DFD&sid=394CD2F50D6790D9&eid=E158A972A605785F&journal_id=1674-4926&journal_name=半导体学报&referenced_num=0&reference_num=11