%T Effect of Hot Accumulative Roll Bonding Process on the Mechanical Properties of AA5083
%A Hassan Sheikh
%A Ebrahim Paimozd
%J Open Journal of Metal
%P 12-15
%@ 2164-277X
%D 2011
%I Scientific Research Publishing
%R 10.4236/ojmetal.2011.11002
%X In this work, accumulative roll bonding (ARB) process as a severe plastic deformation was applied on an AA5083 sheet up to 6 cycles at the temperature of 300¡æ and at the strain rate of 50 s<sup>­©\1</sup>. The results of tensile tests show that the values of the yield stress and the ultimate tensile strength don't change considerably after 4 cycles. Also, transmission electron microscopy (TEM) micrograph confirmed that the microstructure has fine (sub) grains with the size of 200 nm - 400 nm.
%K Grain refinement
%K Aaccumulative Roll Bonding
%K Mechanical Characterization
%K Aluminum Alloys