%0 Journal Article
%T Effect of Substrate Temperature and Dislocation Density on the Epitaxial Growth of YBCO Thin Films on Textured Metal Tapes
%A XU Ya-Xin
%A XIONG Jie
%A XIA Yu-Dong
%A ZHANG Fei
%A XUE Yan
%A TAO Bo-Wan
%J 无机材料学报
%D 2013
%I Science Press
%R 10.3724/sp.j.1077.2013.12385
%X Epitaxial YBa2Cu3O7-δ (YBCO) thin films were grown on Y2O3/YSZ/CeO2 (YYC) buffered Ni-5at%W substrates by direct-current sputtering, and induced by substrate temperature. X-ray diffraction (XRD) results showed that the substrate temperature strongly influenced the epitaxial growth of YBCO films: the a-axis preferential grains grew at lower substrate temperature, and strictly c-axis epitaxial YBCO films were achieved at higher substrate temperature. The amount of a-axis YBCO component evaluated from the ratio of XRD χ-scan integrated intensity of the a-axis and c-axis for the YBCO (102) plane decreased as the substrate temperature increased. Since the development of the a-axis component can result in high angle grain boundaries, which can degrade the Ic passing through the a–b plane, the microstructure and the critical current density of YBCO thin films were improved as substrate temperature increasing. While the microstructure and the critical current density of YBCO thin films were deteriorated above 780  or the baseband oxidation and the interface reaction between the YBCO and the buffer layer. The dislocation density in the YBCO thin films was measured and calculated. The relationship between the dislocation density and critical current density (Jc) was systematically investigated, Jc was much more sensitive to the screw dislocation than to the edge dislocation, which was attributed to the spiral growth mechanism of YBCO thin films.
%K YBa2Cu3O7-δ(YBCO)
%K substrate temperature
%K crystal orientation
%K dislocation density
%U http://www.jim.org.cn/fileup/PDF/20130506.pdf