%T Synthesis of Ordered Mesoporous TiO2 from Industrial Titanyl Sulfate Solution and its Formation Mechanism
%A TIAN Cong-Xue
%A ZHANG Zhao
%J 无机材料学报
%D 2009
%I Science Press
%R 10.3724/sp.j.1077.2009.00225
%X Using composite template (CTAB and P123) as structurea2directing agents, industrial titanyl sulfate as Ti source, the precursor of mesoporous TiO2 was prepared via controlling the hydrolysis and condensation rate of industrial TiOSO4, self-assembly rate of template and pH value of solution. The asa2prepared materials were characterized by XRD, HRTEM, SAED and nitrogen adsorptiona2desorption.Ordered mesoporous anatase titania is obtained after template removal, with hexaganol mesopore, SBET of 205.7m2/g￡ average pore diameter of 3.28nm. The formatiom process of mesopore belongs to cooperative formation mechanism, i.e. the hydrolysis colloid particles of titanium and composite template interact through static force and hydrogen bond on the interface, cooperating to form mesopore.
%K ordered mesoporous titania
%K titanyl sulfate
%K composite template
%K formation mechanism
%U http://www.jim.org.cn/fileup/PDF/20090204.pdf