%T Desarrollo de aceros reforzados con carburos primarios v¨ªa metalurgia l¨ªquida
%A Agote
%A I.
%A Guti¨¦rrez
%A M.
%A Orbegozo
%A M.
%A Asensio
%A M.
%J Revista de Metalurgia
%D 2005
%I Consejo Superior de Investigaciones Cient¨ªficas
%X The steel reinforcement by means of the addition of primary carbides via liquid metallurgy needs to fulfill two essential requirements to be technically viable: the development of a solid reinforcing product which is appropriate to be mixed with the steel and the optimization of the metallurgic addition of these reinforcing particles into the liquid steel. Besides, the improvement of the reinforced alloy characteristics is directly related to the particles' nature of reinforcing particles, their homogeneous and uniform distribution in the matrix and their size and morphology. The manufacture of these carbides by SHS ('Self propagating High temperature Synthesis') and their addition before steel is poured into moulds allows achieving the above-mentioned conditions. Para que el reforzamiento de los aceros con carburos primarios v¨ªa metalurgia l¨ªquida sea t¨¦cnicamente viable se requiere del desarrollo de un tipo de producto reforzante s¨®lido, adecuado para su incorporaci¨®n al acero, as¨ª como de la optimizaci¨®n de dicha v¨ªa metal¨²rgica de adici¨®n del producto reforzante al material base en estado l¨ªquido. Adem¨¢s, la mejora de caracter¨ªsticas de la aleaci¨®n reforzada es funci¨®n directa de la naturaleza de las part¨ªculas, de su homog¨¦nea y uniforme distribuci¨®n en la matriz y del tama o y morfolog¨ªa regular de las mismas. Estas condiciones se consiguen cuando las part¨ªculas de carburo se elaboran previamente mediante la t¨¦cnica SHS (selfpropagating high temperature synthesis) y se a aden al ba o de acero l¨ªquido previo a su colada en moldes o lingoteras.
%K Steel
%K Primary carbides
%K Melting
%K Solidification
%K Wettability
%K Dispersion
%K Reinforcement
%K Acero
%K Carburos primarios
%K Fusi¨®n
%K Solidificaci¨®n
%K Mojabilidad
%K Dispersi¨®n
%K Reforzamiento