%0 Journal Article
%T Failure case of a garage door opener
%A Habib
%A K.
%A Al-Hazzaa
%A A.
%J Revista de Metalurgia
%D 2005
%I Consejo Superior de Investigaciones Cient赤ficas
%X A failure analysis of a garage door opener was conducted for determination of the cause of the failure. The analysis included visual inspections of broken parts as well as electron microscopy examinations of the fracture surface. The visual inspections showed that a bolt connected to the inner trolley of the garage opener assembly was initially fractured. Also, the results of electron microscopy examinations revealed that the broken bolt failed by fatigue damage phenomenon, due to alternating torsional stresses throughout 25 years of an operational life of the garage opener. In addition, a mathematical model corresponding to the failure mechanism was derived along the failure analysis. The model comprises of both design philosophy and fracture mechanics approaches. Se analiz車 el fallo del mecanismo de apertura de una puerta de garaje con el fin de determinar sus causas. El an芍lisis incluy車 una inspecci車n visual de las piezas rotas as赤 como un examen mediante microscop赤a de la superficie de fractura. La inspecci車n visual revel車 que primero se fractur車 un perno conectado al carro interior del mecanismo de apertura. Los resultados del an芍lisis por microscop赤a electr車nica tambi谷n mostraron que el perno roto fall車 debido a fen車menos de da o por fatiga, debido a los esfuerzos torsionales alternos a la largo de 25 a os de vida en servicio del mecanismo de apertura. Por otra parte, se construy車 un modelo matem芍tico correspondiente al mecanismo de rotura durante el an芍lisis del mismo. Este modelo comprende enfoques, tanto de la filosof赤a de dise o como de la mec芍nica de fractura.
%K Failure analysis
%K Fatigue damage
%K Fracture mechanics
%K Scanning electron microscopy (SEM)
%K Mathematical model
%K Modified Goodman diagram
%K An芍lisis de fallo
%K Da o por fatiga
%K Mec芍nica de fractura
%K Microscop赤a electr車nica
%K Modelo matem芍tico
%K Diagrama Goodman modificado
%U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/1052/1064