%0 Journal Article
%T An¨¢lisis de las pel¨ªculas pasivas generadas en aceros inoxidables implantados con cromo
%A Abreu
%A C. Ma
%A Crist¨®bal
%A J.
%A N¨®voa
%A X. R.
%A Pena
%A G.
%J Revista de Metalurgia
%D 2004
%I Consejo Superior de Investigaciones Cient¨ªficas
%X This work studies the effect of chromium implantation on the development of passive layers generated electrochemically in alkaline medium over two stainless steels. The XPS analyses show that the layers generated on the implanted steels present less thickness together with similar composition compared to the unimplanted steels layers. However, SEM micrographs show that the layers grown on implanted steels present more defects and less adherence that the films on unimplanted steels. These changes together with the results obtained by Cyclic Voltammetry suggest an oxide structure modification, lattice structure or cristalinity state. En este trabajo se estudia el efecto de la implantaci¨®n de cromo en el desarrollo de capas pasivas generadas electroqu¨ªmicamente en medio b¨¢sico sobre dos aceros inoxidables (AISI 430 y AISI 304L). Los an¨¢lisis de XPS muestran que las pel¨ªculas desarrolladas sobre ambos aceros implantados presentan espesores menores, junto con composiciones similares, a las formadas sobre los no implantados. Sin embargo, en los resultados del examen con MEB se puede apreciar que las pel¨ªculas tienen m¨¢s defectos (agrietamientos) y peor adherencia (especialmente en el AISI 430). Este cambio, junto con los datos de voltametr¨ªa c¨ªclica, parece sugerir una modificaci¨®n en la estructura de los ¨®xidos, bien en su grado de cristalinidad o bien en la estructura de su red cristalina.
%K Ion implantation
%K stainless steels
%K XPS
%K cyclic voltammetry
%K Implantaci¨®n i¨®nica
%K aceros inoxidables
%K XPS
%K voltametr¨ªa c¨ªclica