The PANI-PVA composite films adopting PVA as the base material and doped
with hydrochloride, DBSA, amino sulfonic acid aqueous solution were prepared
and their conductivity was compared. Among these PANI-PVA composite films, the
conductivity of HCl-PANI-PVA film is the highest. At the same time, the influences
of mass ratio between PANI and PVA, acid content, oxidant content, reaction
time and drying temperature of film on the conductivity of HCl-PANI-PVA film
were studied. The result shows that the conductivity of HCl-PANI-PVA film is the
highest when the mass percentage of PVA is 40%; the C(HC1) = 0.5 mol/L; the n(APS/An) = 1.0; the reaction time is 6
hours and the drying temperature of the film is 80℃, and that the maximum
conductivity of HCl-PANI- PVA film is 16.0 S·cm﹣1.
Cite this paper
Wang, X. (2014). Preparation of PANI-PVA Composite Film with High Conductivity. Open Access Library Journal, 1, e849. doi: http://dx.doi.org/10.4236/oalib.1100849.
Ding, Y. and Yang, J.P. (2008) Emulsion Polymerization Process Research of Phenylamine in DBSA/Water Systems. Acta Polymerica Sinica, 3, 246-250. http://dx.doi.org/10.3724/SP.J.1105.2008.00246
Liu, L., Zhong, F.C. and Wang, X.C. (2008) In-Situ Emulsion Polymerization Polyaniline PANI/PMMA and Its Characterization. Chemical Industry and Engineering Progress, 27, 1230-1233.
Zu, X.H., Hu, J.Q. and Wang, F. (2008) Research and Development of Environmental Friendly Antirust Coatings. Chemical Industry and Engineering Progress, 27, 1394-1399.
Yan, H.Y., Hu, Z.Y. and Ku, K.C. (2005) Research of Conductivity and Spectral Features of Function Sulfonic Acid Doping. Journal of Materials Engineering, 1, 50-52, 57.
Cho, M.S., Park, S.Y., Hwang, J.Y., et al. (2004) Synthesis and Electrical Properties of Polymer Coatings with Polyaniline Nanoparticles. Materials Science and Engineering: C, 24, 15-18.
Ma, L., Feng, L.J. and Gan, M.Y. (2008) Synthesis and Performance Study on PANI with Complex Acid Doping. Chinese Journal of Applied Chemistry, 25, 142-146.