小晶粒丝光沸石合成的研究
邢淑建,寿
分子催化 , 2006,
Abstract: 丝光沸石早在20世纪40年代就由Barfer首次合成出来,由于丝光沸石具有高的硅铝比,因而有优良的耐热、耐酸性能,工业上广泛用作气体或液体混合物分离的吸附剂及石油化工与精细化工催化剂.相对于常规粒度分子筛,小晶粒分子筛具有独特的结构特性,如:更大的外表面积、更多的外表面活性中心和暴露在外的晶胞、短而规整的孔道,从而决定了其具有更大的转化大分子能力,及在其上合成后改性技术更易实现.这些特性使得小晶粒分子筛用于催化裂化、加氢裂化、链烷烃的加氢异构化等炼油工业过程中.因此,如何合成粒径更小以至成为纳米级的丝光沸石近年来引起了人们极大的兴趣,成为催化领域目前受重视的研究课题.
沸石分子筛复合膜的制备及其分离水中微量苯酚和苯的性能
李贤森,寿
催化学报 , 2000,
Abstract: ?
碱处理丝光沸石的表征及其催化合成乙基叔丁基醚的性能
肖强,李自运,孙昕,寿
催化学报 , 2005,
Abstract: ?研究了碱处理对丝光沸石物相、酸性质和催化合成乙基叔丁基醚(ETBE)性能的影响,并采用XRD,NH3-TPD,吡啶吸附的IR,SEM和N2吸附等方法对其进行了表征.结果表明,碱处理含有模板剂的丝光沸石的相对结晶度、酸量、比表面积和孔容都增大.碱处理已脱除模板剂的丝光沸石的相对结晶度、酸量、比表面积和孔容都减小.碱处理含有模板剂的丝光沸石催化合成ETBE的活性明显高于碱处理已脱除模板剂的丝光沸石,在80℃左右即可达到最高活性点,其催化异丁烯的最高转化率为58%,比未经碱处理样品上异丁烯的最高转化率高约13%.
B-Si-ZSM-12型分子筛的合成及其结构和性能的研究
赵亚楠,寿,李赫喧
催化学报 , 1990,
Abstract: ?
不同沸石分子筛对乙基叔丁基醚合成反应的催化性能
李自运,朱岩,寿
催化学报 , 2003,
Abstract: ?研究了液相、加压条件下,不同沸石分子筛对低温合成乙基叔丁基醚(ETBE)的催化性能.发现Hβ沸石的催化活性与A-35树脂催化剂的相当,远远高于其他沸石分子筛催化剂.醇/烯比对Hβ分子筛催化剂及A-35催化剂上ETBE的合成影响比较大.但是Hβ沸石分子筛上ETBE的选择性基本不受醇/烯比的影响,而醇/烯比对树脂催化剂上ETBE的选择性影响相对较大.加入粘合剂后,Hβ沸石分子筛催化剂的活性有所下降,但是加入致孔剂后,其活性有所提高.加入5%聚乙二醇4000后,在温度高于65℃时,Hβ沸石的催化活性已经与A-35的相当,在某些温度下,甚至高于A-35树脂催化剂的活性.
碱性水蒸气处理的ZSM-5沸石酸性质及孔结构的影响
吕仁庆,王秋英,寿
催化学报 , 2002,
Abstract: ?采用XRD,NH3-TPD,比表面积和孔结构测定等研究了在不同温度下用含10%NH3的水蒸气处理时HZSM-5沸石n(Si)/n(Al)=25)酸性质及孔结构的变化规律.结果表明,随着处理温度的提高,HZSM-5的结构未发生明显的变化;样品的总酸量下降很快,但弱酸分布量相对提高,而强酸分布量相对下降;提高处理温度,样品的比表面积和微孔体积减小,二次孔或中孔体积及外表面积有增大的趋势.
Physicochemical characterization and catalytic property study of steam-phosphorus modified HZSM-5
磷酸和水蒸气联合改性的HZSM-5的物化表征及催化研究

Abstract,
吕仁庆
,谷 军,唐 博,寿

燃料化学学报 , 2004,
Abstract: Physicochemical and catalytic properties of steam treated phosphorus-modified-HZSM-5 zeolites have been investigated. XRD and IR show that no new crystalline phase exists in the modified samples. Acidic properties of the samples have been characterized by ammonia temperature programmed desorption (NH_3-TPD), indicating the introduction of phosphorus by impregnation of the zeolite with an aqueous solution of NH_4H_2PO_4 and steam treatment decrease the number of acid sites. After steam treatment, BET surface area decreases remarkably due to the blockage of channel by phosphorus species and dealuminated species. The nitrogen adsorption-desorption measurements suggest that the isothermal type of all samples is a combination of type I and type IV, all hysteresis loops resemble the H4-type in the IUPAC classification. The conversion of n-heptane over steam treated P-modified-HZSM-5 zeolite is higher than that of sole steam treated zeolites, showing a protective effect of the phosphorus against dealumination by hydrothermal treatment at elevated temperature.
纳米丝光沸石分子筛的合成及表征
邢淑建,程志林,于海斌,寿
分子催化 , 2008,
Abstract: 在水热条件下制备丝光沸石的纳米晶.研究了合成条件、不同添加剂、动态晶化等对沸石粒径的影响.结果表明,反应物中较高的碱度,较低的晶化温度,加入NaCl和Na2SO4金属盐做成核助剂,及动态晶化有利于纳米丝光沸石分子筛的合成.
磷酸三乙酯改性HZSM-5沸石的活性及理论研究
吕仁庆,曹作刚,潘行茂,寿,刘晨光
分子催化 , 2005,
Abstract: 采用XRD表征了水蒸气和磷联合改性的HZSM-5沸石分子筛的结构.通过NH3-TPD和N2吸附脱附研究了样品的酸性和比表面.采用正庚烷的裂化反应研究了样品的裂化活性,研究结果表明,磷改性样品与母体样品相比,经过水蒸气处理后显示出较高的酸量和正庚烷裂化活性.上述结果首次用模型簇和计算量子化学方法进行了解释.采用Gaussian94软件包和PM3半经验量子化学方法对模型簇进行了全优化和频率分析.计算结果显示磷改性后样品的脱铝补硅反应热大于母体样品脱铝补硅反应热,从而显示出磷对骨架的稳定化作用.
超声作用下MCM-36分子筛的快速合成
王保玉,吴建梅,李牛,袁忠勇,寿
催化学报 , 2007,
Abstract: ?以四甲基铵硅酸盐为柱化剂,考察了超声作用对MCM-36分子筛合成的影响.结果表明,超声处理显著缩短了柱化剂进入已撑开的MCM-22(P)层间的插层过程的时间.通过控制插层过程的超声时间可以合成出具有不同层间距的MCM-36分子筛,而且合成的MCM-36分子筛内各层的层间距较均一.