退火对聚碳酸酯注塑制品力学及动态力学性能的影响
张勤星,李倩,张果,王利霞,申长雨,张响
化工学报 , 2012, DOI: 10.3969/j.issn.0438-1157.2012.06.040
Abstract: 本文研究了聚碳酸酯(LexanOQ2720)注塑制品退火后的力学及动态力学性能的变化。结果表明,制品的应力集中情况有明显改善,力学性能除断裂伸长率外都产生了较高提升,拉伸强度提高了14.86%,弯曲强度提高了12.7%,弯曲模量提高了21.27%,冲击强度提高了17.93%;动态力学分析结果表明,,注塑制品的内部存在应力。经退火后,注塑制品内部取向、缠结的分子链得到充分松弛,制品储能模量随温度的变化呈线性规律,内部链段的状态稳定,热变形温度得到了提高。而未退火试样的储能模量随温度变化起伏不定,内部链段的状态比较活跃。动态频率对制品中应力有一定响应能力,响应频率范围约为30-60Hz,随着频率扫描温度的升高,由于应力集中降低,频率对应力响应能力不断降低。
纳料金属的力学性能
周宇松,吴希俊
力学进展 , 2001, DOI: 10.6052/1000-0992-2001-1-J2000-016
Abstract: 综述了纳米金属力学性能的研究进展,包括弹性模量、硬度与Hall-Petch关系、拉伸与压缩形变、蠕变与疲劳等力学性能的研究进展。
碳纤维布增强复合材料力学性能评价
郭春红,岳清瑞,杨勇新,才鹏,赵颜,彭福明,李庆伟
工业建筑 , 2006, DOI: 10.13204/j.gyjz200602027
Abstract: 对结构加固用碳纤维布增强复合材料力学性能测试的试件形式和方法做了评估,并建立评价模型对测试结果进行评价。
新型含有机硅二元多嵌段共聚物的研究
史林启,郑国栋,冯之榴
高分子学报 , 1997,
Abstract: 报道了聚羟基醚(PHE)、聚羟基醚砜(PHES)、酚酞聚羟基醚(PPHE)和聚对羟基苯乙烯(PHS)与端胺基聚二甲基硅氧烷(PDMS)通过羟胺缩合生成ABmn新型结构的可溶性含有机硅二元多嵌段共聚物,m值在1~6之间,详细讨论了反应物浓度对共缩聚反应的影响,并通过分子量测定、红外光谱分析和动态力学分析(DMA)技术初步确定了其反应机理、结构和动态力学性能.
热处理对0Cr17Ni5Mo3钢组织和性能的影响
古立新,金建军,刘富荣
材料工程 , 2004,
Abstract: 研究了热处理对0Cr17Ni5Mo3钢显微组织和性能的影响。结果表明,固溶温度在一定范围内对拉伸、冲击性能的影响不明显;470℃时抗拉强度达最高值,在450℃附近时效出现回火脆性,冲击韧性处于低谷。
FeCoNiCuMo高熵合金的组织与性能 The Microstructure and Mechanical Properties of FeCoNiCuMo High-Entropy Alloys  [PDF]
栾军
Material Sciences (MS) , 2013, DOI: 10.12677/ms.2013.32015
Abstract: 采用电弧熔炼和真空吸铸的方法得到FeCoNiCuxMo和FeCoNiCuMox (x表示摩尔比例,取值x = 0.2,0.5,0.8,1)合金。采用X射线衍射仪、扫描电子显微镜、显微硬度仪和万能材料实验机等对上述合金系列的微观组织结构以及力学性能进行了研究。结果表明FeCoNiCuxAl和FeCoNiCuMox高熵合金体系容易形成简单FCC结构和BCC结构的固溶体,它们的显微组织是两种简单结构的混合体,表现为先共晶和共晶相的混合。合金的力学性能与Cu或Mo含量有一定的关联。 FeCoNiCuxMo and FeCoNiCuMox (x values in molar ratio, x = 0.2, 0.5, 0.8, 1) high-entropy alloy system were synthesized using a arc melting method. The microstructures and mechanical properties of the alloys were investigated with X-ray diffraction, scanning electron microscopy (SEM), Vichers hardness testing and universal material testing machine. The both alloys exhibit quite simple FCC and BCC solid solution phases, the microstructures of the alloys are mixing phases of BCC and FCC, which exhibit as pre-eutectic and eutectic phases. The mechanical properties of both alloys are related to the amount of Cu or Mo elements.
超细晶45钢的制备及其组织与力学性能的研究
Study on Microstructure and Mechanical Properties of Ultrafine-Grained 45 Steel
 [PDF]

赵新
Metallurgical Engineering (MEng) , 2014, DOI: 10.12677/MEng.2014.12006
Abstract:
为了制备超细晶粒钢,将45钢淬火后进行了温轧。总变形量为50%。采用光学显微镜和透射电子显微镜研究了这一过程中的微观组织演变。原始组织是板条马氏体组织 + 少量的片状马氏体。试样在600℃~ 700℃变形后的微观结构是纳米碳化物 + 等轴超细晶铁素体,具有良好的综合力学性能,强度和塑性分别达到了646~861 MPa和21.5%~19.1%。
In order to produce ultrafine-grained steel, 45 steel was quenched and warm-rolled. The total re-duction was 50%. The microstructural evolution during the process was studied by using an optical microscope and a transmission electron microscopy. The properties were investigated by using tensile tests. The starting microstructure was lath martensite with a small amount of flake martensite. The microstructure of the specimen compressed at 600?C - 700?C was nano-carbides + equiaxed ultrafine ferrite grains and a good combination of strength and ductility was obtained. The tensile strength and total elongation were 646 - 861 MPa and 21.51% - 9.1%, respectively.

MECHANICAL PROPERTIES AND б-PHASE EMBRITTLEMENT IN A FERRITE-AUSTENITE STAINLESS STEEL AT ELEVATED TEMPERATURES
吴惕言,吴起白,RIQUIERY.
金属学报 , 1993,
Abstract: 研究了铁素体(F)-奥氏体(A)双相不锈钢在600—1100℃范围内的力学性能,其韧性-温度曲线在800-900℃之间有一极小值。阐述了σ相析出动力学及其对材料力学性能的影响,σ相严重损害合金塑性,其影响程度随σ相含量的增加而增高,并与试验温度有极大的关系,1000℃时σ相对拉伸性能影响消失。
EFFECTS OF AGING TEMPERATURE AND TIME ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF GH35A SUPERALLOY
时效温度和时间对一种铁基合金组织和性能的影响

GUO Shouren,LU Dezhong,GUO Jianting,WU Xi Institute of Metal Research,Academia Sinica,Shenyang Fushun Steel Works associate professor,
郭守仁
,卢德忠,郭建亭,吴晰

金属学报 , 1990,
Abstract: 本文研究了GH35A合金在650—750℃,100—10000h时效过程中性能和组织的变化。结果表明,合金室温拉伸强度基本不受时效温度和时间的影响,而室温塑性、韧性及700℃持久寿命在时效至某一时间后开始降低,但下降速度缓慢,直到10000h仍有较高的水平。同时,随时效温度提高,性能降低的开始时间缩短。合金性能的变化主要取决于σ相析出的时间、形态、分布以及σ相的特征。
过渡区应力集中对复合材料强度试验准确度的影响
赵稼祥,胡云涛,张瑞珠
复合材料学报 , 1991,
Abstract: 本文通过推导复合材料强度试验值之准确度与试样破坏部位的关系和破坏发生在试样不同部位的概率,研究了试样过渡区应力集中对复合材料强度试验的影响,讨论了提高试验准确度的措施.