聚烯烃薄膜表面气固相光接枝改性
冯震国,王晓剑
南京工业大学学报(自然科学版) , 1990,
Abstract: 以uv(λ≥320nm)为光源,二苯甲酮为光引发剂,分别以丙烯酸(aa)和α-甲基丙烯酸(maa)为单体,在ldpe和pp薄膜上成功地进行了表面光接枝改性。接枝薄膜用atr-ir光谱方法进行测定和表征。辐照时间增加,接枝程度提高。经300秒反应,接枝ldpe薄膜表而水接触们从103°下降至57°。分别测试了接枝薄膜的表面湿张力及染色性,结果表明:一般接枝程度越高,湿张力越大,表而染色越深且均匀。以maa为单体,在pe上接枝比在pp上容易进行。经pe为基材,用maa接枝改性效果比用aa的要好。
光引发N-乙烯基吡咯烷酮在嵌段聚醚聚氨酯膜上接枝聚合的研究
哈鸿飞,刘先勇,吴季兰,杨福良,冯新德
高分子学报 , 1988,
Abstract: 本文研究了在碱性介质中,氮气氛下N-乙烯基吡咯烷酮(N-VP)在嵌段聚醚聚氨酯(SPEU)膜上的接枝聚合。测定了接枝率与接枝液中N-VP单体浓度、光照时间、催化剂浓度等条件的关系。测定了接枝后SPEU膜的吸水性,并用扫描电镜对膜表面进行了观察。对碱性介质中的接枝机理进行了初步探讨。
PVDF/PEU共混基膜上光接枝制备pH敏感膜的研究
叶艳秋,龚琦,曾振辉,潘雪琴,董声雄
福州大学学报(自然科学版) , 2005,
Abstract: 采用相转化法制备PVDF/PEU共混基膜.在此基膜表面上以二苯甲酮(BP)为光引发剂,丙烯酸(AA)为接枝单体,在紫外光的辐射下引发接枝制备出pH敏感膜.X射线多晶衍射仪(XRD)、扫描电镜(SEM)的表征结果都表明接枝层已经存在于膜表面部分.同时,接枝膜渗透pH值为2~4的水溶液时,渗透通量发生急剧的变化,表现出明显的pH敏感性.
PVDF超滤膜进行聚乙二醇甲基丙烯酸甲酯 (PEGMA)紫外光照射接枝的膜面表征与抗污染分析
潘婷,李方,杜春慧,赵永军,李佳峰,孟蝶,杨波,田晴
环境科学学报 , 2015,
Abstract: 本文采用紫外光照射接枝的方法将聚乙二醇甲基丙烯酸甲酯(PEGMA)亲水单体接枝在疏水性聚偏氟乙烯(PVDF)超滤膜表面,改善PVDF膜的亲水性能.实验中以N,N-亚甲基双丙烯酰胺(MBAA)为交联剂作为对比,发现添加MBAA可以减少PEG接枝层的溶胀性.本实验研究不同改性条件对膜性能的影响,利用表面接触角(CA)、红外光谱分析(ATR-IR)、扫描电镜(SEM)等手段表征膜表面特征,同时研究了改性膜对乳化油和牛血清蛋白溶液分离效率和抗污染能力.实验结果表明,经改性后膜亲水性明显提高,对污染物的截留效果和抗污染能力均有所提高.
低密度聚乙烯丙烯酸气相光接枝体系反应机理的研究
徐绍刚,杨万泰
高分子学报 , 2000,
Abstract: 研究了以二苯甲酮(BP)为光敏剂,丙烯酸在低密度聚乙烯(LDPE)膜上两步法气相光接枝聚合;从反应的基本要素出发,利用紫外光分光光度计跟踪测定了二苯甲酮在LDPE膜中的扩散情况,发现其扩散系数随BP浓度的升高而降低,约在0.8~2.0×10-12m2·s-1之间.同样方法跟踪测定了BP在不同条件下的光还原反应,结果表明当远紫外光被滤掉后,其半衰期大大加长,氧气的存在更是加剧了这一效应;并且通过测定不同条件下气相光接枝聚合的一些基本规律,提出单体扩散为该气相光接枝聚合的控制步骤.
光接枝丙烯酰胺涤棉织物的阻燃性能
金银山,任元林,董二莹,苏倩,信鹏月
纺织学报 , 2013,
Abstract: 本文以二苯甲酮(BP)为光引发剂、丙烯酰胺(AM)为接枝单体,应用光接枝技术将AM接枝到涤棉织物上以改善其阻燃性能。分别对接枝前后涤棉织物进行了红外光谱、力学性能、燃烧性能、极限氧指数、热性能和残炭形貌的测试及分析。结果表明,AM可以通过光接枝技术接枝到涤棉织物表面,接枝后力学性能下降,氧指数、热性能提高。综合观察,接枝AM的涤棉织物的阻燃性明显提高。
SURFACE GRAFTING OF PRE-PEROXIDIZED POLYOLEFINL FILMS BY UV-IRRADIATION
预氧化聚烯烃膜的表面光接枝聚合

HE Ming-bo,HU Xing-zhou,
何明波
,胡兴洲

高分子学报 , 1989,
Abstract: Thermal peroxidized PP films and PE films were graft copolymerized with a light stabilizer,2,2,6,6-tera-methyl-piperidinyl-merhacrylate (MTMP), by UV-irradiation in the absence of sensitizers in order to improve the photostability of films. The influence of various factors, including the thermal peroxidizing time, irradiation time, monomer concentration and the type of solvents, on the grafting content of the peroxidized films was examined. It is shown that the graft copolymerization can not take place in common organic solvents except ketones, and the photostability of either grafted PP or grafted PE film increases greatly compared with that of the ungrafted film.
一种利用梯度光掩模制备梯度表面的简便方法
汪炉林,马育红,周昊,杨万泰
高分子学报 , 2011, DOI: 10.3724/SP.J.1105.2011.10127
Abstract: 以自制杂化双向拉伸聚丙烯/氧化硅(BOPP/SiOx)有机/无机杂化膜为基材,由喷墨打印机直接在杂化膜表面打印色阶图案,制备出对紫外光强度呈梯度透过的梯度光掩模;通过此掩模控制,在双向拉伸聚丙烯(BOPP)和聚对苯二甲酸乙二醇酯(PET)表面实施受限光催化氧化(CPO)光感应羟基化反应、受限光接枝丙烯酸(AA)以及表面沉淀紫外光接枝丙烯酰胺(AM)聚合反应.全反射红外光谱(ATRFTIR)、X射线光电子能谱(XPS)、水接触角、荧光显微镜及扫描电镜(SEM)分析表明,分别得到表面能、接枝层厚度及接枝链密度呈梯度分布的功能性梯度表面.
纳米SiO2锚固光敏基团引发MMA光接枝聚合研究
刘晓暄,**,白迎坤,荆燕妮,王洪波,陈兵,吴光国
高分子学报 , 2007,
Abstract: 对纳米SiO2进行了锚固光引发剂的表面修饰,进而引发甲基丙烯酸甲脂(MMA)光接枝聚合制备有机/无机复合粒子.纳米SiO2粒子首先用氯化亚砜进行表面氯化,再与光引发剂2-羟基-4-(2-羟基乙氧基)-2-甲基苯丙酮(Irgacure2959)反应从而锚固上光引发剂.通过紫外光引发MMA在经过修饰过的纳米SiO2表面上进行表面光接枝聚合.采用IR、TGA和TEM等方法表征了接枝前后纳米粒子的变化,证明了表面接枝物的存在,并研究了不同反应条件对单体转化率、接枝率和接枝效率的影响.研究结果表明,搅拌对接枝过程的影响比较显著.TGA结果显示未搅拌聚合时接枝率只能达到比较小的程度,而在搅拌条件下180min内MMA的接枝率可达到110%.
紫外光接枝改性磺化聚醚砜微孔膜及其pH敏感性
冯翠平,李井峰,许振良,杨虎,施江焕
华东理工大学学报 , 2008,
Abstract: 用紫外光接枝聚合方法将丙烯酸(AA)接枝到磺化聚醚砜(SPES)微孔膜上,得到具有pH敏感性的分离膜.接枝膜采用衰减全反射(ATR-IR)附件进行了表征,接枝膜表面及断面形态采用扫描电子显微镜(SEM)进行观察,并同时通过接枝率、水渗透通量和截留率的测定研究了接枝膜的接枝程度、渗水性能和pH敏感性.通过紫外光接枝聚合的方法,在磺化聚醚砜微孔膜的膜表面和孔内接枝上了丙烯酸接枝层作为pH感应型开关;当丙烯酸质量分数为0.05,光照20min时,接枝率达到8.40%,pH=2时的纯水渗透通量约为中性时的20倍;当牛血清蛋白(BSA)渗透液的pH小于其等电点4.7,pH为2~4时,截留率发生显著变化,表现出明显的pH敏感性.