%T Effect of Calcium Carbide Waste Powder on Some Engineering Properties of Bamboo Leaf Ash Concrete
%A Olumuyiwa Samson Aderinola
%A Olasunkanmi Eniola Omolola
%A Ajibola Ibrahim Quadri
%J Open Access Library Journal
%V 5
%N 11
%P 1-15
%@ 2333-9721
%D 2018
%I Open Access Library
%R 10.4236/oalib.1104990
%X
The assessment of cement partially replaced with calcium carbide waste pow-der, CCWP and bamboo leaf ash, BLA on the strength of concrete made with cement was investigated. Oxide composition analysis of CCWP and BLA con-firm their status as non-pozzolanic material rich in CaO component and poz-zolanic materials, respectively. Setting times, slump, compressive and micro-structure analysis tests were conducted on fresh and hardened concrete. Twen-ty-eight (28) and fifty-six (56) days peak compressive strength values of 13.23 N/mm2 and 15.97 N/mm2 respectively were obtained when 5% CCWP was mixed with 5% BLA plus 90% cement. Values comparable to 28 and 56 days peak compressive strength values of 13.03 N/mm2 and 15.07 N/mm2 respec-tively obtained when cement was only used as a binder. The use of CCWP and BLA in concrete will ensure economy in concrete production and a better way of disposing these wastes.
%K Calcium Carbide Waste Powder (CCWP)
%K Bamboo Leaf Ash (BLA)
%K Cement
%K Concrete
%K Compressive Strength
%K Workability
%K Setting Time
%K Interfacial Bond